Use of vanadium oxide and/or aluminum bronzes as a cathode material in electrochemical generators

ABSTRACT

The use of vanadium oxide iron and/or aluminium bronzes as a cathode material in electrochemical generators is described. The cathode material is a vanadium oxide bronze having formula: M 1   x1  M 2   x2  V 2  O 5 , wherein M 1  is a vanadium oxide bronze or iron, M 2  is a metal different from M 1  having valency n and chosen from alkali metals, alkaline earth metals, transition metals and aluminium, and x 1  and x 2  are such that 0.06≦x 1  ≦0.13; 0≦x 2  ≦0.20; and 0.27≦3x 1  ≦nx 2  ≦0.39; and may be combined as a cathode (9) with an Li or Li alloy anode (5) and with an electrolyte consisting of lithium perchlorate in propylene carbonate.

This is application is a national phase of a application PCT/FR92/01167 with publication number WO 93/12550.

The present invention relates to the use of vanadium oxide bronzes as a cathode material in electrochemical generators.

It more particularly applies to secondary electrochemical generators, whose operation is based on the intercalation of a metal ion, such as lithium in the cathode material.

For close to twenty years, the use of primary, lithium electrochemical generators has provided energy sources with better performance characteristics than conventional batteries with respect to the energy density, the life and the operation in a wide temperature range. Such primary generators are particularly used for the supply of equipment requiring low current densities, such as watches, calculators and for maintaining memories.

In view of the good performance characteristics of these primary lithium generators, much research has been carried out with a view to producing secondary lithium generators having the characteristics inherent in lithium anode batteries and the longer life of accumulators. The development of such generators involves the reversibility of the reactions at both the anode and the cathode.

In addition, much research has been devoted to investigating cathode materials able to reversibly insert metal ions such as lithium ions. Among these considerable research has been directed at those based on vanadium pentoxide V₂ O₅, which have high performance characteristics as a result of the standard, very high potential of V⁵⁺ and the compatibility of the oxidation potential of these materials with the stability range of the organic electrolytes conventionally used in electrochemical generators. Moreover, V₂ O₅ has a structure intermediate between the tunnel structure of rutile-type oxides and that of MoO₃ -type oxide laminas.

The operating characteristics of a secondary electrochemical generator using V₂ O₅ as the electrode material will largely depend on the reversibility of the insertion reaction of a metal such as lithium (Li⁺) in the host lattice of the V₂ O₅, in accordance with the following reaction diagram:

    V.sub.2 O.sub.5 +xe.sup.- +xLi.sup.30 ⃡Li.sub.x V.sub.2 O.sub.5

Thus, the aim is to obtain a good reversibility of this process and preferably for a high voltage, with a maximum faradic capacitance, i.e. a maximum lithium x insertion level over a large number of galvanostatic cycles.

With regards to the V₂ O₅ cycling behaviour, it is known that the constant current reduction of V₂ O₅ in a conventional electrolytic medium takes place in four separate stages as described by Kumagai et al in Electrochimica Acta, 28, 1983, pp 17-22.

FIG. 1 illustrates the typical V₂ O₅ discharge curve in propylene carbonate containing 1 mole/l of LiClO₄ at 20° C. using V₂ O₅ at the cathode and a lithium anode.

FIG. 1, which represents the evolution of the potential as a function of the exchanged lithium quantity, shows that the first two stages of said reduction, which are characterized by a potential above 3 V and a Li_(y) V₂ O₅ composition range with 0≦y≦1, corresponding to the conventional cycling of Li/V₂ O₅ generators for which a perfect reversibility is observed. The third range corresponds to a partial reversibility loss, whose mechanism has not been completely explained, and a complete irreversibility is observed after a deep discharge involving more than 2.4 lithium ions.

Much research has also been carried out with a view to improving the cyclability of materials similar to V₂ O₅ in order to bring about a greater reduction involving the third and fourth insertion stages located at 2.2 and 1.8 V. Electrode materials with a greater reduction are described e.g. by Cocciantelli et al in Journal of Power Sources, 34, 1991, pp 103-111 and in FR-A-2 655 777, as well as by Delmas et al in Journal of Power Sources, 34, 1991, pp 113-188 and WO 90/11623.

Thus, in said two documents the mass capacitance of an electrochemical generator has been increased by increasing the lithium insertion level.

Other research carried out on vanadium pentoxide-based materials has led to the production of metal oxide bronzes such as Na₀.33 V₂ O₅ by a sol-gel process, in order to improve the performance characteristics of such materials, as described in FR-A-2 616 013.

As a result of recent research, other cathode materials based on vanadium pentoxide bronze have been developed, which have improved properties compared with V₂ O₅ as a result of the presence of appropriate elements.

The invention relates to an electrochemical generator comprising an anode, a cathode comprising a vanadium pentoxide-based cathode material and a conductive electrolyte containing ions which can be intercalated in the cathode material, characterized in that the cathode material is a vanadium pentoxide bronze of formula:

    M.sup.1 x.sub.1 M.sup.2 x.sub.2 V.sub.2 O.sub.5

in which M¹ represents the trivalent aluminium or iron, M² represents a metal different from M¹ of valency n chosen from among alkali metals, alkaline earth metals, transition metals and aluminium, and x₁ and x₂ are such that

0.06≦x₁ ≦0.13;

0≦x₂ ≦0.20; and

0.27≦3x₁ +nx₂ ≦0.39.

In said vanadium pentoxide bronze, the presence of metal M¹ (iron or aluminium) gives the cathode material an electronic conductivity well above that of V₂ O₅, as well as the possibility of inserting more lithium than in V₂ O₅.

Moreover, the possible presence in said material of a second metal M², e.g. sodium, makes it possible to adapt the characteristics of the material to the contemplated uses applications by producing a mixed structure with two imbricated lattices, e.g. a two-phase system with the coexistence of an orthorhombic phase and a monoclinic phase.

Generally, when M² is a metal other than Al or Fe, the quantity of M² is low, i.e. x₁ is at least 0.06.

As examples of alkali metals and alkaline earth metals which can be used for M², reference can be made to lithium, sodium, potassium, calcium and magnesium.

The transition metals used for M² are the metals of periods 3 to 12 of the 18 column table of the periodic classification, i.e. scandium, yttrium, lanthanides, actinides, titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, tungsten, manganese, technetium, rhenium, iron, ruthenium, osmium, cobalt, rhodium, iridium, nickel, palladium, platinum, copper, silver and gold.

In the case of these transition metals a choice is e.g. made of iron, cobalt, copper, chromium or zirconium.

Preferably, according to the invention, use is made of a bronze of formula M¹ x₁ V₂ O₅ with M¹ having the meaning given hereinbefore and x₁ such that 0.09≦x₁ ≦0.13 or a bronze of formula Fe_(x1) Al_(x2) V₂ O₅ with x₁ and x₂ having the meanings given hereinbefore.

The bronzes used as the cathode material in the invention can be prepared by conventional processes, particularly by that described in FR-A-2 616 013.

This process consists of carrying out an ion exchange on a vanadium pentoxide xerogel in order to replace the H⁺ cations of said gel by M¹ and optionally M² atoms, e.g. by immersing the gel in an aqueous solution of a salt of M¹ optionally containing a salt of M². Following said ion exchange, a heat treatment is carried out at a moderate temperature chosen as a function of M¹ and M₂.

According to the invention, the bronze complying with the above formula is used as the cathode material in an electrochemical generator comprising a cathode, an anode and a conductive electrolyte containing ions which can be intercalated in said material.

In this generator, the anode can be based on lithium, e.g. of lithium, lithium alloy or a lithium insertion compound such as compounds based on carbon or oxide, e.g. tungsten oxide.

The electrolytes used can be liquid electrolytes, solid electrolytes or lithium ion conductive polymers.

When use is made of a liquid electrolyte, the latter can be constituted by a solution of lithium salt in an appropriate solvent, generally an organic and aprotic solvent, which can e.g. be chosen from within the group of cyclic ethers and esters having a straight chain and mixtures thereof.

As examples of an organic solvent which can be used, reference can be made to propylene carbonate, ethylene carbonate, tetrahydrofuran, dioxolan and 1,2-dimethoxyethane.

The organic solvent can also be constituted by a sulphone, e.g. dimethyl sulphone, with a view to operating in the temperature range 80° to 180° C.

The lithium salts can e.g. be chosen from among lithium perchlorate, lithium tetrafluoroborate, lithium trifluoromethane sulphonate, lithium hexafluorophosphate, lithium hexafluoroarsenate and mixtures thereof.

When use is made of a solid electrolyte, the latter can be constituted by a lithium glass e.g. obtained from P₂ S₅, Li₂ S and LiI or B₂ S₃, Li₂ S and LiI.

In the case where the electrolyte is constituted by a polymer, it can be a polyethylene oxide filled with a lithium salt, like those described hereinbefore.

To be usable in the generator according to the invention, the cathode material is generally mixed with an electronic conductive material such as carbon black, graphite and/or carbon fibres or powder. In this case, it is possible to prepare the electrode by mixing a bronze powder of formula M¹ _(x1) M² _(x2) V₂ O₅ with carbon black, graphite and/or carbon powder or fibres, followed by the compression of said mixture to the desired form. It is also possible to deposit the mixture on a current lead e.g. constituted by an electronic conductive material grid such as stainless steel or nickel. It is also possible to mix a bronze powder according to the invention with acetylene black, graphite and polytetrafluoroethylene and then inlay said material on a stainless steel grid.

BRIEF DESCRIPTION OF DRAWINGS

Other features and advantages of the invention can be better gathered from the following non-limitative description and with reference to the attached drawings, wherein show:

FIG. 1, already described, the discharge curve of V₂ O₅, i.e. the potential as a function of the number of inserted lithium ions.

FIGS. 2 to 5 are X-ray diffraction spectra of cathode materials according to the invention.

FIG. 6 Diagrammatically and in vertical section a lithium electrochemical generator according to the invention.

FIG. 7 A redox voltamperogram of the cathode material FeO₀.11 V₂ O₅ according to the invention.

FIG. 8 A redox voltamperogram of the V₂ O₅ cathode material given for comparison purposes.

FIG. 9 A reduction chronopotentiogram of the cathode material Fe₀.11 V₂ O₅ illustrating the potential as a function of the number of inserted lithium ions for curve 1, the current density is 500 μA/cm², for curve 2 the current density is 200 μA/cm², and for curve 3 the current density is 100 μA/cm².

FIG. 10 The reduction chronopotentiogram for constant current density of 500 μA/cm² of the following cathode materials: V₂ O₅, Al₀.11 V₂ O₅, and Fe₀.11 V₂ O₅.

FIG. 11 The reduction chronopotentiogram with constant current density of 40 uA/cm² of the cathode materials V₂ O₅ and Fe₀.11 V₂ O₅ used in pure form.

FIG. 12 A graph showing the specific capacitance as a function of the number of galvanostatic cycles performed in the potential range 3.7 to 1.7 V for the cathode materials: Fe₀.11 V₂ O₅, Al₀.11 V₂ O₅ and V₂ O₅.

FIG. 13 A graph showing the evolution of the specific capacitance as a function of the number of galvanostatic cycles performed in the potential range 3.8 to 2.1 V for the cathode materials V₂ O₅, Fe₀.11 V₂ O₅ and Al₀.11 V₂ O₅.

The following examples illustrate the preparation of the cathode materials used in the invention.

Example 1: Preparation of Fe₀.11 V₂ O₅

Preparation firstly takes place of a vanadium pentoxide V₂ O₅ gel by acidifying a solution of a sodium salt such as sodium metavanadate in such a way as to obtain decavanadic acid, which polymerizes spontaneously in water at ambient temperature in order to give by polycondensation the vanadium pentoxide gel corresponding to the formula:

    (H.sup.+.sub.0.33 (V.sub.2 O.sub.5).sup.0.33-,1.6H.sub.2 O).

Following the deposition of the gel on a glass plate and drying in air, ion intercalation takes place in order to replace the H⁺ cations by iron immersing the thin vanadium pentoxide xerogel layer on the glass plate in an aqueous 0.1 mole/l iron nitrate solution. After reacting for 30 min, the xerogel plate is removed and abundantly rinsed with distilled water, followed by drying at ambient temperature. This gives the hydrated intercalatlon product of formula Fe₀.11 V₂ O₅, 2.35H₂ O. The intercalation product then undergoes a heat treatment at 535° C. for approximately 1 h in a furnace open to the air. This gives the metal bronze of formula Fe₀.11 V₂ O₅.

FIG. 2 shows the X-ray diffraction spectrum in reflection geometry of the thin film product obtained in this way.

The spectrum obtained shows a preferred and extremely marked orientation of the 001 planes corresponding to the existence of horizontal planes stacked in accordance with the axis c. Only the lines 001 and 002 are visible with relative intensities of 100 and 27. This spectrum is typical of an alpha orthorhombic bronze phase.

FIG. 3 shows the X-ray diffraction spectrum of the ground product.

Table 1 gives the relative intensities of the diffraction lines of said thin film bronze in powder form.

                                      TABLE 1                                      __________________________________________________________________________     hk1   200                                                                               001                                                                               101                                                                               110                                                                               400                                                                               011                                                                               310                                                                               002                                                                               102                                                                               600                                                                               020                                        Ground                                                                                12                                                                               100                                                                                18                                                                                43                                                                                38                                                                                12                                                                                20                                                                                15                                                                                7  7  15                                        Thin film                                                                            /  100                                                                               /  /  /  /  /   27                                                                               /  /  /                                          __________________________________________________________________________

Example 2: Preparation of Al₀.11 V₂ O₅

The same operating procedure as in example 1 is followed for preparing said orthorhombic bronze, except that for the intercalation of the aluminium use is made of a 0.1 mole/l aluminium nitrate solution and the heat treatment is performed at 600° C. for 1 hour.

This gives the orthorhombic bronze of formula Al₀.11 V₂ O₅.

The X-diffraction spectra of the thin film product and the ground product are respectively shown in FIGS. 4 and 5.

As in the case of iron, only the lines 002 and 001 are visible on the spectrum of the thin film product.

The metal bronzes obtained in examples 1 and 2 can be used as cathode material in the electrochemical generator of FIG. 6. For this use, a mixture of graphite and bronze powder is prepared containing 90% by weight graphite and this is compressed to the desired shape.

FIG. 6 shows that the generator comprises two metal screws 1 and 3 placed in a polytetrafluoroethylene envelope (2), between which are successively arranged an anode (5) constituted by a freshly cut, diameter 14 mm aluminium and lithium alloy LiAl disk, a glass fibre separator (7), a cathode constituted by a disk (9) with a surface of 1 cm² and a thickness of 0.5 mm formed from a mixture of approximately 20 mg of powders containing 10% by weight bronze and 90% by weight graphite obtained previously and an electrolyte impregnating the glass fibre separator (7) and the cathode (9).

The electrolyte is constituted by a solution of lithium perchlorate in distilled propylene carbonate containing 1 mole (106.4 g) of lithium perchlorate per litre and use is made of 0.2 ml of this electrolyte for impregnating the separator (7) and the positive electrode (9).

The assembly of the two electrodes and the separator is compressed by the metal screws (1) and (3), which also serve as current collectors. The voltage of the above generator is approximately 3.5 V.

The electrochemical properties of the cathode material formed by Fe₀.11 V₂ O₅ is tested by carrying out a voltamperometric cycling of the electrode at a speed of 0.13 mV/s. The voltamperogram obtained under these conditions and which illustrates the intensity in pA as a function of the potential in V based on Li/Li⁺ is shown in FIG. 7.

For comparison purposes, FIG. 8 shows the voltamperogram obtained under the same conditions when the electrode material is constituted by orthorhombic V₂ O₅ mixed with graphite in the same proportions.

It is clear from FIGS. 7 and 8 that the cathode material according to the invention has an excellent reversibility, which is not the case with V₂ O₅.

FIG. 9 shows the reduction chronopotentiograms of the cathode material Fe₀.11 V₂ O₅ under different current densities in the potential range between 3.6 and 1.8 V, based on the electrode Li/Li⁺.

Curve 1 refers to a current density of 500 μA/cm², curve 2 to a current density of 200 μA/cm² and curve 3 to a current density of 100 μA/cm².

The shape of the curves confirms the results obtained by the voltamperometric method. More specifically, the insertion of lithium in the cathode material according to the invention takes place in several stages. The first two stages are at an average potential of 3.1 V corresponding to the insertion of approximately 0.9 lithium ion per mole of bronze, the third stage at 2.2 V involves approximately 0.8 lithium ion per mole of bronze and the fourth at about 1.9 V corresponds to the insertion of approximately 0.5 lithium ion per mole of bronze. It is also possible to take account of a complimentary stage at about 2.9 V, where there is a slow and continuous potential drop in place of the sudden potential drop conventionally observed with V₂ O₅ following the insertion of one lithium ion per mole of V₂ O₅.

Thus, the maximum faradic capacitance available during the insertion of the lithium in the bronze Fe₀.11 V₂ O₅ is approximately 360 Ah/kg.

The influence of the current density on the reduction signal of the bronze reveals an interesting behaviour to the extent that the shape of the signal and the faradic capacitance are not dependent on the current density in the range 100 to 500 μA/cm².

FIG. 10 shows the reduction chronopotentiograms at a constant current density of 500 μA/cm² (i.e. potential variations in V based on Li/Li as a function of the number of Li ions inserted per mole of material), relative to cathode materials constituted by a mixture of graphite powder and powder of V₂ O₅, Al₀.11 V₂ O₅ or Fe₀.11 V₂ O₅ incorporating 90% graphite.

In the case of iron or aluminium bronzes according to the invention there is a slow and continuous decrease of the potential between 3 and 2.2 V, a faradic balance relative to the first two stages comparable to that of V₂ O₅, even under high discharge conditions and the presence of a third insertion stage in the form of powerful discharge conditions, which does not exist in the case of V₂ O₅.

FIG. 11 shows the reduction chronopotentiograms at a constant current density of 40 μA/cm² of cathode materials constituted solely by pure V₂ O₅ or pure Fe₀.11 V₂ O₅. In this case, the faradic capacitance of the iron bronze according to the invention is much higher than that of V₂ O₅.

There is also an evaluation of the performance characteristics of the iron bronze in galvanostatic cycling on four reduction stages. The results are given in FIG. 12, which also shows the results obtained under the same conditions with aluminium bronze Al₀.11 V₂ O₅ and V₂ O₅. These cyclings were carried out under a current density of 200 μA/cm in a potential range of 3.7 to 1.7 V including the four insertion stages.

FIG. 12 illustrates the specific capacitance as a function of the number of cycles.

The results obtained reveal the potential of iron bronze, which is a very high performance material, because 65% of the initial faradic capacitance (approximately 400 μh/kg) is still available after the thirtieth cycle (i.e. 200 μh/kg), whereas in the case of V₂ O₅, the specific capacitance is only 50 μh/kg, i.e. 20% of the initial faradic capacitance after 30 cycles. Therefore iron bronze has much superior performance characteristics to V₂ O₅.

In the same way, aluminium bronze has superior performance characteristics to V₂ O₅, because the specific capacitance is approximately three times that of V₂ O₅ after 30 cycles.

FIG. 13 shows the results obtained in galvanostatic cycling performed on only three reduction stages, i.e. between 3.9 and 2.1 V/Li/Li⁺ with a current density of 200 uA/cm² on the following cathode materials: Fe₀.11 V₂ O₅, Al₀.11 V₂ O₅ and V₂ O₅.

In this case, the specific capacitance in Ah/kg is lower, but as previously for Fe₀.11 V₂ O₅ and for Al₀.11 V₂ O₅, it remains higher than that of V₂ O₅ after 30 cycles. 

We claim:
 1. Electrochemical generator comprising an anode, a cathode comprising a vanadium pentoxide-based cathode material, and a conductive electrolyte containing ions which can be intercalated in the cathode material characterized in that the cathode material is a vanadium pentoxide bronze of formula:

    M.sup.1.sub.x1 M.sup.2.sub.x2 V.sub.2 O.sub.5

in which M¹ represents trivalent aluminum or iron, M² represents a metal different from M¹ of valency n chosen from among alkali metals, alkaline earth metals, transition metals and aluminum, n being equal to 1, 2, or 3, and x₁ and x₂ are such that 0.06≦x₁ ≦0.13; 0≦x₂ ≦0.20; and 0.27≦3x₁ +n₂ 23 0.39.
 2. Electrochemical generator according to claim 1, characterized in that the cathode material complies with the formula:

    Fe.sub.x1 V.sub.2 O.sub.5

with 0.09≦x₁ ≦0.13.
 3. Generator according to claim 1, characterized in that the cathode material complies with the formula:

    Al.sub.x1 V.sub.2 O.sub.5

with 0.09≦x₁ ≦0.13.
 4. Generator according to either of the claims 2 and 3, characterized in that x₁ =0.11.
 5. Electrochemical generator according to claim 1, characterized in that the cathode material complies with the formula:

    Fe.sub.x1 Al.sub.x2 V.sub.2 .sub.5

in which x₁ and x₂ are as defined in claim
 1. 6. Generator according to any one of the claims 1, 2, 3, and 5 characterized in that the anode is of lithium, lithium alloy, or lithium insertion compound.
 7. Generator according to claim 6, characterized in that the electrolyte is constituted by a solution of lithium salt in an organic solvent.
 8. Generator according to claim 7, characterized in that the electrolyte is a solution of lithium perchlorate in propylene carbonate. 